Product Description
6031AB expoxy resin is specially developed for hand-lay up, it can be cured fastly at the lower or the room temperature.The laminate has good strength , stiffness and tenacity performance.
The laminate has good acid and alkali resistance, good waterproof and oil resistance, and good dustproof performance, good heat resistance and good ageing resistance.
Appearance and properties:
| Item |
M6031A, epoxy resin |
|
M6031B,curing agent |
| Color |
Transparent liquid |
|
Pale yellow |
| |
| Viscosity25ºC |
About 13500 |
|
About 1300 |
| Storage Life 25ºC |
1 Year |
|
1Year |
| Operational Time ( 3:1 mix,25ºC) min |
|
20 |
Usage:
1.According to the proportion, A, B fully mix, to prevent curing incomplete.
2.Please operate as soon as fully mix,and as far as possible finish in the available time.
3.During curing process, please clean utensils and containers in time, in order to avoid glue solidification on the tools and products.
Use ratio: weight A: B = 100:33 volume A: B = 3:1
Product Feature:
1.Mixed products has low viscosity, high reactivity, normal temperature or low temperature curing.
2.Curing products have excellent water resistance and aging resistance.
3.The product has high heat deformation temperature (when not with fiberglass, also can reach 80 ºC)
4.Completely cured products has good acid and alkali resistant, superior Solvent resistance.High hardness, good toughness.
5.Applicable to epoxy anticorrosive, electronic potting and other places.
Notes:
1.This product will start curing after mixed , the viscosity will rise soon, and gives off heat.
2.The curing speed is fast, please control the mixed amount at one time.The more mixed, the faster the reaction, the curing speed will be faster, the working time will be shorter,and may be let out a lot of heat, may lead to flash polymerization.
3.There are very few people who contact for a long time will have mild skin irritation, itch had mild pain, it is recommended to wear protective gloves when use.If skin touch,please wipe with acetone or alcohol, and use cleaner clean.
| 1.Mechanical property |
| Properties of resin casting bodies(for reference) |
| 25ºC*24H+70ºC12H |
|
|
| Tensile strength (Mpa) |
≥55 |
62 |
| Tensile modulus (Mpa) |
≥2700 |
2913 |
| Elongation rate(%) |
≥2.5 |
3.82 |
| Bending strength (Mpa) |
≥100 |
105 |
| Bending modulus (Mpa) |
≥2800 |
3100 |
| Impact toughness (Kj/m2) |
≥30 |
32.3 |
| DSC (Tg) ºC |
≥70 |
80 |
| Ratio |
---- |
A/B=3/1 |
The above data had gotten under the ideal conditions in the laboratory, due to the various conditions, the final data will have some deviations, whether applicable, please make sure after testing the sample. The final interpretation of the above data belongs to my company.
The performance date of FRP will be more prominent .(the mechanical properties of epoxy resin has a little influence on FRP.)
The performance data of FRP are basically the same if FRP cured completely, even if the different resin to be used, but DSC date excepted.
2. The corrosion medium
To compared with vinyl and unsaturated resin, epoxy resin generally has better corrosion resistance, FRP products made by modified epoxy resin, are more suitable for corrosion resistance
| Medium |
Concentration (%) |
Temperature (ºC) |
Y/N |
| Soybean oil |
100 |
80 |
Y |
| Ethyl Alcohol |
All |
Room temperature |
Y |
| Oleic Acid |
100 |
80 |
Y |
| Hydrochloric acid |
Saturation concentration |
80 |
Y |
| Sodium Hydroxide |
All |
50 |
Y |
| Sulfuric acid |
1~75 |
75 |
Y |
| Carbamide |
|
65 |
Y |
The above data had gotten under of our knowledge of the conditions, due to the various conditions, the final data will have some deviations, whether applicable, please make sure after testing the sample. The final interpretation of the above data belongs to my company.
Give us a chance, and we' ll return you with satisfaction.