Fiberglass Tissue Glass Veil Mat Thick 0.4mm for Battery Separator

• Shape: Tissue
• Fiber Characteristics: E-Glass
• Diameter of Filaments: Intermediate Fibers
• Fiber Appearance: Continous Fiber
• Glass Composition: E-Glass
• Roll Length: 250m-2000m
• Model NO.: S-BM0.4
• Thickness: 0.3mm-1.0mm
• Binder Content: 16%
• Glass Type: E Glass
• Area Weight(G/M2): 52.2
• Tensile Strength MD(N/50mm): 159
• Transport Package: Pallet
• Specification: A Grade
• Origin: China
• HS Code: 70193900
• Production Capacity: 10 Million M2/Month

Product Description

Product Description

The battery separator tissue is chiefly used as the base material of lead acid battery separator. 
It is raw material of glass fiber separator, PE+glass separator, PVC+glass separator.

Feature:
Good acid resistance, high porosity, small pore size, high liquid absorptivity and low electric resistance.
Good vibrating resistance, starting ability, few permanganate reducate and longer service life.
The surface is flat and smooth, with uniform thickness.
Capable of preventing short circuits and absorbing needed electrolyte. 

Product Parameters

 

Binder  (%)	Thickness (mm)10KPA	MD (N/5cm)	Acid resistance (%) ( 72hours)	Acid resistance (%) (15mins)	Wetting time(s)	Fe   (%)	Cl (%)
16	GBZ 0.3	≥60	<3.00	<2.00	<5	≤0.008	≤0.003
16	GBZ 0.4	≥80	<3.00	<2.00	<5	≤0.008	≤0.003
15	GBZ 0.5	≥100	<3.00	<2.00	<5	≤0.008	≤0.003
15	GBZ 0.6	≥120	<3.00	<2.00	<5	≤0.008	≤0.003
15	GBZ 0.7	≥140	<3.00	<2.00	<5	≤0.008	≤0.003
13	GBZ 0.8	≥160	<3.00	<2.00	<5	≤0.008	≤0.003
13	GBZ 1.0	≥190	<3.00	<2.00	<5	≤0.008	≤0.003

S-BM0.40 Technical Date:
 

Item	Standard	Test Result
Area Weight(g/m2)	≥40	52.2
Binder Content(%)	15±2	16.75
Thickness(mm)	0.40±0.03	0.43
Tensile Strength MD(N/50mm)	≥60	159
Acid Resisitance 72hours(%)	≤3	1.89
KmnO4 Reduzate Content(ml/g)	≤15	13.25
Wetting Time(s)	≤100	7.2
According to Criterion	Q/320412 CXB005--2014

 
Test Condition:Ambient temperature 20ºC,Relative humidity 65%.
 
Packing:
The product is wound tightly into a roll on a paper core. Each roll is wrapped into a plastic bag and placed in a carton box.Then put into a pallet.

Storage condition:
Unless otherwise specified, it is recommended to store in a cool and dry condition. The product must remain in packaging material until just prior to its use.

Picture

Give us a chance, and we' ll return you with satisfaction.