Unsaturated Polyester Resin for Hobas Pipe

• Molecular Principal Chain: Element Organic Polymer
• Color: Light Yellow
• 220kg/Drum: 80 Drum in 20FCL
• Shelf Time: 6 Month
• Viscosity 25 Degree PA.S: 0.12-0.24
• Gel Time 25 Degree Min: 28-56
• Model NO.: TK10600
• Solid Content: 58-64
• Appearance: Light Yellow Clear Liquid
• Acid Value: 27-35mgkoh/G
• Transport Package: Drum
• Specification: A Grade Quality
• Origin: China
• HS Code: 39079100
• Production Capacity: 10000ton/Year

Product Description

Product Description

TK10600 is an orthophthalic type unsaturated polyester resin with middling viscosity and high reactivity . It has excellent mechanical performance ,High elongaion at break and impact strength,good mechanical strength. This resin is speical designed for  HOBAS pipe body structure.

Technical Data Sheet

 

Technical Indexes of Liquid Resin
Item	Unit	Value	Standard
Appearance		Straw yellow Liquid	Visual
Chroma (Pt-Co)			GB7193.7-92
Acid Value	mgKOH/g	18-22	GB2895-82
Viscosity(25ºC)	mPa.S	400-600	GB7193.1-87
Gel Time	min	8-10	GB7193.6-87
exothermic peak	ºC	165-180	GB7193.6-87
post-cure time	min	9-15	GB7193.6-87
Non-Volatile	%	60-64	GB7193.3-87
Thermal Stability (80ºC)	h	48	GB7193.5-87
Note: Gel Time is 25°C; in air bath; 0.5 ml cobalt isocaprylate solution and 0.5 ml MEKP solution were added into 50 g resin

 
 

Performance Indexes of Resin Casting Substance
Item	Unit	Value	Standard
Barcol Hardness       ≥	Barcol	40	GB3854-1983
Tensile Strength       ≥	MPa	70	GB2568-1995
Tensile Modulus      ≥	MPa	3000	GB2568-1995
Elongation at Break    ≥	%	3.5	GB2568-1995
Flexural Strength      ≥	MPa	90	GB2570-1995
Flexural Modulus     ≥	MPa	3200	GB2570-1995
Impact Strength       ≥	KJ/m^2	15	GB2571-1995
H.D.T              ≥	ºC	80	GB1634-1989
Note: Environmental Temperature for Experiment: 23±2°C; relative humidity: 50±5%

 