60kg/M3 Cross Linked Rigid PVC Foam Core Plain for Ship Building

• After-sales Service: Any Time
• Warranty: 6months
• Feature: Environmental, Fireproof, Light Weight
• Fire Rating: Other
• Certification: ISO9001
• Customized: Customized
• Model NO.: P60
• Material: PVC
• Property1: Impact Resistance
• Property2: Low Water Absorption
• Property3: Insulation
• Processing Temperture: -240 to +100degree
• Density: 48-250kg/M3
• Application1: Wind Energy
• Application2: Marine
• Application3: Motor Home
• Transport Package: Carton, Pallet
• Specification: A Grade
• Trademark: UTEK
• Origin: China
• HS Code: 3921
• Production Capacity: 1000000m2/Month

Product Description

Product Description

PVC foam material, as a close cell foam, based on vinyl polymer, modified with the throughout Aramids link. It is the compounding chemical material based on PVC and PUR. It can be used as the core material in the sandwich structure.
 

Properties

It is closed cell cross linked regid PVC foam, with excellent specific modulus and strength.It have outstanding fatigue properties, inpact resistance and low water absorption. It also has good insulation properties.It has both the good size stability and machinability, compatible with various sandwich structure processing methods, compatible with various resin systems. It is the ideal core material for te light weight high strength sandwich composite core material. The processing temperture ranges from -240ºC to +100ºC, the long term operation temperature ranges from -240ºC to +80ºC.It has good water resistance and not rotten. It has good fire resistance.It can widely be used in wind energy, marine, sports, railway and aerospace industries. The density ranges 45-250 kg/m3

Detailed Photos

 

 

Product Parameters

Item	Standard	Unit		P45	P60	P80	P100	P130	P200	P250
Density	ISO 845	Kg/m^3	msmv	48	60	80	100	130	200	250
Density(Nominal)	ISO 845	Kg/m^3	msv	/	54	72	/	/	/	/
Tensile strength	ASTM C297	Mpa	msv	1.4	1.8	2.5	3.5	4.5	7.1	9.2
Tensile strength	ASTM C297	Mpa	msmv	1.1	1.5	2.2	2.5	3.5	6.3	8
Tensile modulus	ASTM C297	Mpa	msv	55	75	95	130	175	250	360
Tensile modulus	ASTM C297	Mpa	msmv	45	57	85	105	135	210	320
Compressive strength	ISO 844	Mpa	msv	0.6	0.93	1.4	2	3	4.8	6.2
Compressive strength	ISO 844	Mpa	msmv	0.5	0.7	1.15	1.65	2.4	4.2	5.4
Compressive modulus	ISO 844	Mpa	msv	50	70	90	135	170	240	300
Compressive modulus	ISO 844	Mpa	msmv	45	60	80	115	145	200	240
Shear strength	ISO 1922	Mpa	msv	0.5	0.76	1.15	1.44	2.1	3.5	4
Shear strength	ISO 1922	Mpa	msmv	0.46	0.63	0.95	1.4	1.9	3.2	3.9
Shear modulus	ISO 1922	Mpa	msv	15	20	27	35	50	85	104
Shear modulus	ISO 1922	Mpa	msmv	12	16	23	28	40	75	88
Shear elongation,at break	ISO 1922	%	msmv	8	10	15	15	20	20	20
Shear elongation,at break	ISO 1922	%	msv	/	20	30	/	/	/	/

 

 