The resin, thickening agent, release agent, filler, mixed high temperature curing agent, coating in the 2 film, the glass fiber filament after cutting machine cut into 25mm short strips, sprinkle in the coating resin paste film, the 2 layer composite thin film, from Finn and American Fram, Inc (www.Finnandfram.COM) kneading professional SMC sheet unit import, the glass fiber soaked through automatic packaging, folding machine, and then in the drying room temperature through thickening time, achieve the molding viscosity requirements, namely into finished products. Appearance: Zig-zag package, outside the aluminum film
Sanitary grade SMC gives finished products glossy surface. It has low shrinkage and is water-resistant.
|Density( g/cm³)||GB1463-88||1.82|| |
|Glass fiber content(%)||GB/T15568-95||≥22|| |
|Water absorption(%)||GB1462-88||≤0.2|| |
|Average Shrinkage (%)||GB/T15568-95||≤0.02|| |
|Tensile Strength(Mpa)||GB1447-83||≥50|| |
|Flexural Strength(Mpa)||GB1449-83||≥120|| |
|Impact Strength( kJ/m²)||GB1451-83||≥50|| |
Used for molding drinking water tank, automobile bumper, electrical products, bathroom products
Have smooth surface, beautiful color, high-strength, excellent insulating performance, anti-corrosion, high production efficiency. They are widely used in many fields such as electronics, electrical, auto parts, water tank, instrument, civil installation and decoration. Proper SMC/BMC should be selected according to product's structure, performance and mould.
Pressure MPa 5-15
Temperature º C 145± 5
Maintaining time: Min/mm 1.
|SMC-A (electric)||High mechanical strength products such as high/low voltage switch box, insulation plates|
|SMC-B (flame retardant)||High mechanical strength and flame retardant products such as signal lamps, cable tray|
|SMC-C (high-strength)||Special high mechanical strength products such as hammer handle|
|SMC-D (general purpose)||Non-electric products such as chair, water tank|
|BMC-A (electric)||Electric parts with common mechanical strength|
|BMC-D (general purpose)||Non-electric press mould products with common mechanical strength|